Dictionary – H

 

HALF HARD TEMPER

(A) No. 2 Temper. In low carbon cold-rolled strip steel, produced by cold rolling to a hardness next to but somewhat softer than full hard temper. (B) In brass Stainless Steel Strip, tempers are based on minimum tensile or yield strength. For Chromium-Nickel grades Half-Hard Temper 150,000 TS., 110,000 YS. Min.


HARD DRAWING

Drawing metal wire through a die to reduce cross section and increase tensile strength.


HARD DRAWN

Wire or tubing drawn to high tensile strength by a high degree of cold work.


HARD DRAWN SPRING STEEL WIRE

A medium high carbon cold drawn spring steel wire. Used principally for cold springs.


HARDENABILITY

The ability of a metal, usually steel, to harden in depth as distinguished from the terms “hardness.”


HARDENED AND TEMPERED SPRING STEEL STRIP

A medium or high carbon quality steel strip which has been subjected to the sequence of heating, quenching and tempering.


HARDENING

Any process which increases the hardness of a metal. Usually heating and quenching certain iron base alloys from a temperature either within or above the critical temperature range.


HARDNESS

Degree to which a metal will resist cutting, abrasion, penetration, bending and stretching. The indicated hardness of metals will differ somewhat with the specific apparatus measuring hardness. (See Brinell HardnessRockwell HardnessVickers HardnessScleroscope HardnessTensile Strength also is an indication of hardness.


HARD TEMPER

(A) For Steel see Full Hard Temper. (B) In brass mill terminology. Hard Temper is four B & S numbers hard or 37.1 % reduction.


HEAT OF STEEL

The product of a single melting operation in a furnace, starting with the charging of raw materials and ending with the tapping of molten metal and consequently identical in its characteristics.


HEAT TREATMENT

Altering the properties of a metal by subjecting it to a sequence of temperature changes, time of retention at specific temperature and rate of cooling therefore being as important as the temperature itself. Heat treatment usually markedly affects strength, hardnessductilitymalleability, and similar properties of both metals and their alloys.


HIGH BRASS

65% – A copper-zinc alloy containing 35% zinc. Possesses high tensile strength and is used for springs, screws, rivets, etc.


HOOKE’S LAW

Stress is proportional to strain in the elastic range. The value of the stress at which a material ceases to obey Hooke’s law is known as the elastic limit.


HOT DIP

In steel mill practice, a process whereby ferrous alloy base metals are dipped into molten metal, usually zinctin or terne, for the purpose of fixing a rust resistant coating.


HOT SHORT

Brittleness in hot metal.


HOT TOP

(See Sinkhead)


HOT WORKING

Plastic deformation of metal at a temperature sufficiently high not to create strain hardening. The lower limit of temperature for this process is the recrystallization temperature.


HYDROGEN EMBRITTLEMENT

(1) Brittleness of metal, resulting from the occlusion of hydrogen (usually as a by-product of pickling or by co-deposition in electroplating). (2) A condition of low ductility resulting from hydrogen absorption and internal pressure developed subsequently. Electrolytic copper exhibits similar results when exposed to reducing atmosphere at elevated temperature.


HYPEREUTECTOID STEEL

steel having more than the eutectoid percentage of carbon. (See Eutectoid Steel)


HYPOEUTECTOID STEEL

Steel with less than eutectoid percentage of carbon. (See Eutectoid Steel)